Chemical sensor development based on polycrystalline gold electrode embedded low-dimensional Ag2O nanoparticles
Chemical sensor development based on polycrystalline gold electrode embedded low-dimensional Ag2O nanoparticles
 
لغة الوثيقة : الانجليزية 
المستخلص : We have prepared low-dimensional silver oxide nanoparticles (NPs) by a sono-chemical method using reducing agents in alkaline medium. The resulting NPs were characterized by UV/vis and FT-IR spectroscopy, X-ray powder diffraction (XRD), X-ray photoelectron spectroscopy (XPS), X-ray energy dispersive spectrometry (XEDS), and field-emission scanning electron microscopy (FESEM). They were deposited on a flat-polycrystalline gold electrode (AuE, surface area, 0.0216 cm(2)) to give a sensor with a fast response toward 4-nitrophenol (4-NPh) in liquid phase. The sensor also displays good sensitivity and long-term stability, and enhanced electrochemical performances. The calibration plot is linear (r(2) = 0.9873) over the large concentration range (LDR, 1.0 mu M to 0.5 mM). The sensitivity and detection limit is calculated to similar to 4.740 mu A cm(-2) mM(-1) and similar to 0.19 mu M (signal-to-noise ratio, at a SNR of 3), respectively. We also discuss possible future prospective uses of this metal oxide nanomaterials in terms of chemical sensing. (C) 2013 Elsevier Ltd. All rights reserved. Keywords 
ردمد : 0013-4686 
اسم الدورية : ELECTROCHIMICA ACTA 
المجلد : 112 
العدد : 112 
سنة النشر : 1434 هـ
2013 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Sunday, July 16, 2017 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
M RahmanRahman, M باحث  
S KhanKhan, S باحث  
A AsiriAsiri, A باحث  
A Al-SehemiAl-Sehemi, A باحث  

الملفات

اسم الملفالنوعالوصف
 42031.pdf pdf 

الرجوع إلى صفحة الأبحاث